| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTM D-792 | 1.77 | |
| 机械性能 | IZOD冲击强度 | 3.2mm | ASTM D-256 | 85 | J/m |
| 断裂伸长率 | 3.2mm | ASTM D-638 | 1.4 | % |
| 弯曲强度 | 3.2mm | ASTM D-790 | 177 | MPa |
| 拉伸强度 | 3.2mm | ASTM D-638 | 132 | MPa |
| 弯曲模量 | 3.2mm | ASTM D-790 | 15200 | MPa |
| 热性能 | 模压温度范围 | | | 30-95 | ℃ |
| RTI,Mechanical with Impact | 3.0mm | UL 746-B | 220 | ℃ |
| RTI,Mechanical with Impact | 3.0mm | UL 746-B | 240 | ℃ |
| RTI,Mechanical with Impact | 1.0mm | UL 746-B | 240 | ℃ |
| 玻璃化转变温度 | | ASTM D-3418 | 120 | ℃ |
| RTI,Electrical | 3.0mm | UL 746-B | 240 | ℃ |
| RTI,Mechanical with Impact | 1.0mm | UL 746-B | 210 | ℃ |
| 干燥温度 | | | 135 | ℃ |
| 熔点 | | ASTM D-3418 | 335 | ℃ |
| RTI,Electrical | 1.0mm | UL 746-B | 240 | ℃ |
| 热变形温度 | 1.80MPa | ASTM D-648 | 272 | ℃ |
| 解链温度范围 | | | 350-360 | ℃ |
| 其它性能 | Rating@Thickness | | UL 746-B | V-0 | |
| Thickness Tested | | UL 94 | 1.5 | mm |