代理燃料电池用PTFE、电池粘接剂用PTFE聚四氟乙烯水溶液、Dyneon PTFE TF 5035Z美国3M公司 简介：该型号为PTFE聚四氟乙烯水性溶液，固体含量58%，用于含水的不粘涂料、不粘涂层，工业建筑，燃料电池，油漆和涂料，橡胶和塑料等用 突出特性： 粒度双峰分布； 优良的成膜性； 低孔隙度； 高光泽； 优异的电气性能； 硬度较大。 3M? Dyneon? PTFE Dispersion TF 5035Z is a milky-white, water-based fluoropolymer dispersion. The dispersion has a solids content of around 58 percent solids. The spherical hydrophobic polymer particles have an average size of around 200 nm. The polymer has a density of approximately 2. 2 g/ml. TF 5035Z is used for formulating aqueous non-stick coating systems, which can be used to coat suitably prepared metal, glass and ceramic surfaces and cookware. Details Improved film formation. Far fewer pores. Better gloss. Better adhesion. Lower processing costs. Higher hardness. 美国3M公司PTFE乳液系列产品： 3M Dyneon PTFE TF 5050Z 水性溶液，固体含量58%， 3M Dyneon PTFE TF 5060GZ 水性溶液，固体含量59% 3M Dyneon PTFE TF 5033Z 水性溶液，固体含量24% 3M Dyneon PTFE TF 5035Z 水性溶液，固体含量58% PTFE溶液为乳白色液体，系四氟乙烯聚合后在非离子表面活性剂存在下的分散浓缩液，聚四氟乙烯固体含量在60%（wt）左右。经分散浓缩液处理后的制品，具有卓越的化学腐蚀能力，如耐强酸、强碱、强氧化剂等，有突出的耐热、耐寒及耐摩性，长期使用温度范围为-200℃—+250℃。还有优异的电绝缘性，且不受温度与频率的影响。 主要用途： 可直接用于浸渍多孔材料如石棉制品、玻璃纤维、陶瓷和电碳制品等。可用以制得抗粘防腐涂层；也可用其涂覆玻璃布并制得层压制品；还可直接纺丝制得特种合成纤维。广泛应用于国防工业、橡胶工业、电子电池工业等部门。 使用注意事项： 1. 接触本品时请勿吸烟。 2. 本品存放在10-30℃左右环境中。避免强烈日光直晒。在0℃会结冰，引起凝聚使产品报废。自生产起保质期为半年，储存期间每隔15日应进行轻微摇荡。 3. 本品按非危险品运输，运输时避免日晒、雨淋。采用PE塑料桶包装，25kg/桶或35kg/桶。 聚四氟乙烯分散液浸渍制品加工说明书（参考） PTFE分散液是平均粒径为0.2μm-0.3μm,PTFE树脂悬浮在液态水中形成的胶体溶液粘度0.015Pa·s-01020Pa·s,浓度为60%左右,PH值9-10。用PTFE分散液浸渍石棉、玻璃纤维、玻璃布、多孔金属材料所制得的制品具有优良的性能,不吸水,具有良好的不粘性、润滑性与气密性,在高温时仍具有优良的耐化学腐蚀性且比未浸渍的坯料具有更高的机械强度。 (1)PTFE浸渍石棉 一般采用45%左右的PTFE分散液,浸渍后在100℃左右干燥,用来编织圆形或方形的动密封件。 (2)PTFE浸渍玻璃纤维 玻璃纤维必须清洗后才浸渍在PTFE分散液中,100℃下干燥,然后在280℃-290℃烘焙再烧结。 (3)PTFE浸渍多孔金属 由多孔金属浸渍PTFE所形成的产品称氟塑料金属,可加工成轴承、活塞环、导向套、导轨、球型支承座等部件,广泛应用于化工、机械、汽车、交通、纺织,电机等行业中。 所有多孔金属必须具有30%-40%孔隙率。PTFE分散液浓度60%,采用真空浸渍,真空度98.5KPa,在100℃±10℃干燥4小时。然后在370℃±10℃烧结炉中用惰性气体保护烧结。